The production process of titanium plate
With the improvement of the level of technology, in the industrial production, many products, parts continue to process and innovate, titanium plate is a product of industrial innovation.
What is titanium plate? It is drawn into the titanium sheet through titanium metal, there are two kinds of performance standards of titanium plate, national standard and American standard. National standard is GB/3621-2007, GB/T13810-2007, American Standard is ASTM B265, ASTM F136, ASTM F67, AMS4928. Titanium plate is made by hot processing, cold processing and annealing, and a series of production process.
What is the manufacturing process of titanium plate in the end?
1.Hot forging: forging process above metal recrystallization temperature.
2.Hot rolling: the rolling process is carried out at a higher temperature than the recrystallization temperature.
3.Cold rolling: the rolling process is that the plastic deformation temperature is lower than the recovery temperature.
4.Annealing: it is a kind of metal heat treatment process that make the metal be slowly heated to a certain temperature and maintained at sufficient time, and then cooled at suitable speed.
5.Pickling: The workpiece is immersed in sulfuric acid and other aqueous solutions to remove oxide thin films on the surface of metal. it is pre-treatment or intermediate treatment of electroplating, enamel, rolling and other processes.
The above is the simple introduction of the production process of titanium plate.
What is titanium plate? It is drawn into the titanium sheet through titanium metal, there are two kinds of performance standards of titanium plate, national standard and American standard. National standard is GB/3621-2007, GB/T13810-2007, American Standard is ASTM B265, ASTM F136, ASTM F67, AMS4928. Titanium plate is made by hot processing, cold processing and annealing, and a series of production process.
What is the manufacturing process of titanium plate in the end?
1.Hot forging: forging process above metal recrystallization temperature.
2.Hot rolling: the rolling process is carried out at a higher temperature than the recrystallization temperature.
3.Cold rolling: the rolling process is that the plastic deformation temperature is lower than the recovery temperature.
4.Annealing: it is a kind of metal heat treatment process that make the metal be slowly heated to a certain temperature and maintained at sufficient time, and then cooled at suitable speed.
5.Pickling: The workpiece is immersed in sulfuric acid and other aqueous solutions to remove oxide thin films on the surface of metal. it is pre-treatment or intermediate treatment of electroplating, enamel, rolling and other processes.
The above is the simple introduction of the production process of titanium plate.